Low EMA flexural modulus
Problem Phenomenon
EMA product flexural modulus <20% of design value
Cause Analysis
EMA soft with low modulus; filler addition insufficient or poor interface without reinforcing effect; crystallinity too low
Solution
1) Add 10-15wt% rigid filler to increase modulus; 2) Nucleating agent to increase crystallinity; 3) Select high modulus grade
Key Takeaway
Low flexural modulus is caused by material softness and insufficient filler; adding rigid filler is key