Large EVOH Creep Deformation
Problem Phenomenon
EVOH product creep under long-term load >5%, exceeding the 2% requirement
Cause Analysis
EVOH elastomer nature has large creep; molecular weight too low, creep resistance poor; not crosslinked, plastic flow large
Solution
1) Select high molecular weight grade; 2) Slight crosslinking 0.3wt% DCP to reduce plastic flow; 3) Add rigid filler to reduce creep
Key Takeaway
Large creep is caused by elastomer nature; slight crosslinking and rigid filler are key