Degradation Problem in Compression Molding of PAK Special Engineering Plastic
Problem Phenomenon
Polyacrylate ketone PAK shows degradation during compression '2079851475616104453ing at 240-300°C.
Cause Analysis
Improper control in the aspect of PAK high-temperature mold temperature).
Solution
Inert gas protection.
Key Takeaway
PAK high-temperature processing requires precise control.