Q
Poor Plating Adhesion of Biaxially Oriented Polypropylene Film ABS Products
A
The electroplating quality of ABS is closely related to the material grade and internal stress.
Thermoforming plating adhesionABSinternal stresselectroplating graderelease agent
16 views
Read Full Answer →
Q
Performance Degradation of Biaxially Oriented Polypropylene Film Material Caused by Thermal Degradation
A
Thermal degradation is the main risk in processing; controlling temperature and reducing residence time are the key.
Extrusion & Post thermal degradationmolecular weight decreasebarrel temperatureresidence timescrew speed
16 views
Read Full Answer →
Q
Annealing Treatment of Biaxially Oriented Polypropylene Film Products to Improve Stress
A
Annealing treatment is an effective method to reduce the residual stress of products.
Extrusion & Post annealingresidual stressheat deflection temperaturedimensional stabilitystress cracking
16 views
Read Full Answer →
Q
thickness deviation Occurring in the cooling and sizing Stage of Biaxially oriented polypropylene film
A
The process parameters of each stage of film production need to be precisely controlled; equipment condition and raw material quality are the foundation.
Extrusion & Post cooling and sizingthickness deviationbiaxially oriented polypropylene filmprocess parametersequipment maintenance
16 views
Read Full Answer →
Q
material waste Occurring in the die discharge Stage of Biaxially oriented polypropylene film
A
The process parameters of each stage of film production need to be precisely controlled; equipment condition and raw material quality are the foundation.
Extrusion & Post die dischargematerial wastebiaxially oriented polypropylene filmprocess parametersequipment maintenance
16 views
Read Full Answer →
Q
efficiency decline Occurring in the corona treatment Stage of Biaxially oriented polypropylene film
A
The process parameters of each stage of film production need to be precisely controlled; equipment condition and raw material quality are the foundation.
Extrusion & Post corona treatmentefficiency declinebiaxially oriented polypropylene filmprocess parametersequipment maintenance
16 views
Read Full Answer →
Q
quality fluctuation Occurring in the longitudinal stretching Stage of Biaxially oriented polypropylene film
A
The process parameters of each stage of film production need to be precisely controlled; equipment condition and raw material quality are the foundation.
Extrusion & Post longitudinal stretchingquality fluctuationbiaxially oriented polypropylene filmprocess parametersequipment maintenance
16 views
Read Full Answer →
Q
Elongation at Break of Biaxially Oriented Polypropylene Film Not Up to Standard
A
Film performance needs to be systematically optimized from three aspects: raw materials, process, and cooling.
Extrusion & Post elongation at breakfilmbiaxially oriented polypropylene filmextrusion temperaturestretching process
16 views
Read Full Answer →
Q
Insufficient Weather Resistance/Yellowing of Biaxially Oriented Polypropylene Film ASA Products
Q
Surface Roughness Appearing on the Surface of Biaxially Oriented Polypropylene Film
A
Film surface defects need to be controlled from three aspects: extrusion temperature, die condition, and cooling conditions.
Material Drying surface roughnessfilm surfacebiaxially oriented polypropylene filmdie conditionchill roll
9 views
Read Full Answer →