Cold material entering the mold too early

The material enters the mold when the mold has not reached the set temperature. When this defect appears in products of Process No. 3, it is usually related to a specific process parameter range or equipment state. If it continues to appear, it will directly affect the product qualification rate and production rhythm, increasing material loss and rework costs. Timely diagnosis and elimination is a basic requirement for ensuring stable production.

1. Mold design factors: insufficient mold preheating, operation rhythm too fast, inaccurate mold temperature detection, heating system failure. 2. Molding pressure factor: In compression molding, pressure is not only used to overcome flow resistance, but also directly affects the compactness of the product and the degree of fiber impregnation; insufficient pressure is an important cause of product looseness and insufficient strength.

1. Process parameter optimization and adjustment: ensure the mold is fully preheated to the set temperature, adjust the operation rhythm, calibrate the temperature detection, overhaul the heating system. 2. Systematic troubleshooting method: Troubleshooting of compression molding problems follows the order of 'material -> temperature -> pressure -> mold'. First check the preheating and flowability of the material, then verify the mold temperature distribution and curing time, then adjust the molding pressure and mold closing speed, and finally check the mold venting and demolding conditions. 3. Preventive management: Establish standardized process parameter cards and quality control limits for each set of mold/product, and regularly conduct process capability index (CPK) evaluations. For recurring problems, use fishbone diagrams or 5Why analysis to trace the root cause, and solidify the countermeasures as PFMEA control points.

This problem is a typical manifestation of cold material entering the mold too early in compression molding; the core of the solution lies in proper preheating of the material and assurance of flowability, as well as precise matching of mold temperature and molding pressure. It is recommended to adjust coordinately from both aspects of material state and process parameters.