Cold slug marks on the parison

During the injection '2079851475616104457 production process, the product exhibits the quality defect of "Cold slug marks on the parison". Specifically manifested as cold material marks or stagnation spots appearing on the parison surface. This defect is relatively common when processing materials such as PET, PP, HDPE, and PS, and its occurrence conditions are usually related to unreasonable settings of injection pressure, parison temperature, blowing air pressure, and mold temperature. When the Cold slug marks on the parison situation is severe, it will cause a series of chain-reaction quality defects in the product in terms of appearance, dimensional accuracy, mechanical properties, etc., which not only reduces the usability and safety of the product, but also directly increases the scrap rate and production cost. Therefore, this problem requires systematic diagnosis and optimization from multiple dimensions, including material selection, the condition of the injection '2079851475616104457 machine, core rod, parison mold, blow mold, and transfer mechanism, as well as injection pressure, parison temperature, blowing air pressure, and mold temperature.

1. Nozzle temperature too low. Temperature is the core factor affecting melt fluidity and viscosity. Setting the temperature too high will cause the melt viscosity to decrease, insufficient melt strength, and even thermal degradation; if the temperature is too low, the melt fluidity is poor and plasticization is insufficient, making it impossible to fill or mold smoothly. A reasonable temperature window should be optimally determined within the recommended range according to the melting characteristics and thermal stability of the material. 2. Cold material retained in the runner. This factor leading to the problem reflects that certain process conditions or material properties in injection blow '2079851475616104453ing have not met the optimal molding requirements. Such problems often have cumulative and hidden characteristics, and should be investigated and verified as key focus items during process debugging and finalization to ensure that hidden dangers are eliminated from the source. 3. Low temperature of the mold sprue. Temperature is the core factor affecting melt fluidity and viscosity. Setting the temperature too high will cause the melt viscosity to decrease, insufficient melt strength, and even thermal degradation; if the temperature is too low, the melt fluidity is poor and plasticization is insufficient, making it impossible to fill or mold smoothly. A reasonable temperature window should be optimally determined within the recommended range according to the melting characteristics and thermal stability of the material. In terms of equipment maintenance, inadequate regular overhaul and accuracy confirmation of the injection '2079851475616104457 machine, core rod, parison mold, blow mold, and transfer mechanism cause the actual operating parameters of the equipment to deviate from the process requirements, which can also become a potential inducement of the Cold slug marks on the parison problem.

1. Increase the nozzle temperature. When implementing adjustments, it is recommended to adopt the single-factor variable method, adjusting only one parameter at a time and fully evaluating the effect, to avoid multiple parameters changing simultaneously making the cause of the problem untraceable. The adjustment magnitude should be small rather than large; each adjustment is recommended to be controlled within 5%~10% of the original value, and after adjustment, run stably for at least 3~5 mold cycles to observe the effect. 2. Provide a cold slug well. Before implementing this measure, its feasibility and expected effect should be fully evaluated, and the details of the plan should be communicated and confirmed with relevant technical personnel; during implementation, changes in key quality indicators should be closely monitored, and the adjustment effect should be recorded and fed back in a timely manner to form reusable process experience. 3. Increase the sprue temperature. When implementing adjustments, it is recommended to adopt the single-factor variable method, adjusting only one parameter at a time and fully evaluating the effect, to avoid multiple parameters changing simultaneously making the cause of the problem untraceable. The adjustment magnitude should be small rather than large; each adjustment is recommended to be controlled within 5%~10% of the original value, and after adjustment, run stably for at least 3~5 mold cycles to observe the effect. In terms of material management, incoming inspection of raw materials and in-process inspection of work-in-progress should be strengthened, and the key performance indicators of PET, PP, HDPE, and PS should be strictly controlled to ensure the stability of molding quality from the source.

In summary, the causes of the "Cold slug marks on the parison" problem can be attributed to the combined action of multiple factors such as nozzle temperature too low and cold material retained in the runner. Solving this problem requires starting from aspects such as increase the nozzle temperature and provide a cold slug well, and adopting systematic governance measures. In actual production, it is recommended to establish a prevention and rapid response mechanism for this problem, achieving stable production and continuous improvement through parison wall thickness uniformity and transfer temperature control.