Uneven bottle neck sealing surface

During the injection '2079851475616104457 production process, the product exhibits the quality defect of "Uneven bottle neck sealing surface". Specifically manifested as unevenness appearing on the bottle neck sealing surface. This defect is relatively common when processing materials such as PET, PP, HDPE, and PS, and its occurrence conditions are usually related to unreasonable settings of injection pressure, parison temperature, blowing air pressure, and mold temperature. When the Uneven bottle neck sealing surface situation is severe, it will cause a series of chain-reaction quality defects in the product in terms of appearance, dimensional accuracy, mechanical properties, etc., which not only reduces the usability and safety of the product, but also directly increases the scrap rate and production cost. Therefore, this problem requires systematic diagnosis and optimization from multiple dimensions, including material selection, the condition of the injection '2079851475616104457 machine, core rod, parison mold, blow mold, and transfer mechanism, as well as injection pressure, parison temperature, blowing air pressure, and mold temperature.

1. Wear of the core rod end face. Mechanical wear and loosening during long-term equipment operation will cause clearance changes, accuracy degradation, and unstable operation, thereby triggering various process and quality problems. Establishing a regular inspection and preventive maintenance system for equipment operating conditions, and promptly repairing or replacing worn parts, is a necessary measure to maintain equipment accuracy and process stability. 2. Insufficient mold machining accuracy. The mold is the core tool that imparts shape and surface quality to the product. Unreasonable mold design, such as improper runner/gate dimensions, insufficient venting, inadequate draft angle, etc., will directly cause molding defects. The machining accuracy, surface treatment quality, and daily maintenance condition of the mold also directly affect product quality. In addition, insufficient overall coordination between parison wall thickness uniformity and transfer temperature control is also a factor that cannot be ignored; there are complex interactions and coupling relationships among the various process parameters, and the deviation of any single parameter may aggravate the degree of Uneven bottle neck sealing surface through chain effects. In terms of equipment maintenance, inadequate regular overhaul and accuracy confirmation of the injection '2079851475616104457 machine, core rod, parison mold, blow mold, and transfer mechanism cause the actual operating parameters of the equipment to deviate from the process requirements, which can also become a potential inducement of the Uneven bottle neck sealing surface problem.

1. Regrind the core rod end face. The polishing operation should proceed step by step from coarse to fine; each time a finer abrasive is used, the polishing direction should be changed to eliminate the texture marks of the previous step. The final surface roughness should be tested with a roughness meter to confirm that it meets the standard. After polishing is completed, it should be thoroughly cleaned to remove residues of abrasives and grinding agents to prevent them from entering the melt and contaminating the product. 2. Improve the mold machining accuracy. When implementing adjustments, it is recommended to adopt the single-factor variable method, adjusting only one parameter at a time and fully evaluating the effect, to avoid multiple parameters changing simultaneously making the cause of the problem untraceable. The adjustment magnitude should be small rather than large; each adjustment is recommended to be controlled within 5%~10% of the original value, and after adjustment, run stably for at least 3~5 mold cycles to observe the effect. It is recommended to formulate a preventive checklist for the Uneven bottle neck sealing surface problem, incorporate parison wall thickness uniformity and transfer temperature control into the scope of daily inspections, and conduct online monitoring of key parameters through the SPC statistical process control method to achieve early warning and rapid response to problems. In terms of material management, incoming inspection of raw materials and in-process inspection of work-in-progress should be strengthened, and the key performance indicators of PET, PP, HDPE, and PS should be strictly controlled to ensure the stability of molding quality from the source.

In summary, the causes of the "Uneven bottle neck sealing surface" problem can be attributed to the combined action of multiple factors such as wear of the core rod end face and insufficient mold machining accuracy. Solving this problem requires starting from aspects such as regrind the core rod end face and improve the mold machining accuracy, and adopting systematic governance measures. In actual production, it is recommended to establish a prevention and rapid response mechanism for this problem, achieving stable production and continuous improvement through parison wall thickness uniformity and transfer temperature control.