Gel particles on the parison surface (fisheyes)

In the injection '2079851475616104457 production process, the product exhibits the quality defect of "Gel particles on the parison surface (fisheyes)".The specific manifestation is Incompletely plasticized gel particles appear on the parison surface.This defect is more common when processing materials such as PET, PP, HDPE and PS, and its occurrence is usually related to unreasonable settings of injection pressure, parison temperature, blowing pressure and mold temperature.When the Gel particles on the parison surface (fisheyes) situation is severe, it will cause a series of chain quality defects in the product's appearance, dimensional accuracy, mechanical properties and other aspects, which not only reduces the product's functionality and safety in use, but also directly increases the scrap rate and production cost.Therefore, this problem requires systematic diagnosis and optimization from multiple dimensions such as material selection, the status of the injection '2079851475616104457 machine, core rod, parison mold, blow mold and transfer mechanism, and injection pressure, parison temperature, blowing pressure and mold temperature.

1. Insufficient plasticization temperature.Temperature is the core factor affecting melt fluidity and viscosity.Excessively high temperature settings will cause decreased melt viscosity, insufficient melt strength and even thermal degradation; excessively low temperature results in poor melt fluidity and insufficient plasticization, making smooth filling or forming impossible.A reasonable temperature window should be optimally determined within the recommended range according to the melting characteristics and thermal stability of the material. 2. High-melting-point resin mixed into the raw material.Material selection and handling are the foundation of forming quality.The intrinsic properties of the resin such as molecular weight, molecular weight distribution and melt index determine its processing window and final performance.Factors such as excessive moisture content of raw materials, mixed impurities and improper regrind ratios will all cause various defects during processing. In addition, the insufficient overall coordination of parison wall thickness uniformity and transfer temperature control is also a factor that cannot be ignored; there are complex interactions and coupling relationships among the process parameters, and the deviation of any parameter may aggravate the degree of Gel particles on the parison surface (fisheyes) through chain effects. In terms of equipment maintenance, the regular overhaul and accuracy confirmation of the injection '2079851475616104457 machine, core rod, parison mold, blow mold and transfer mechanism are not in place, causing the actual operating parameters of the equipment to deviate from process requirements, which will also become a potential inducement of the Gel particles on the parison surface (fisheyes) problem.

1. Raise the plasticizing zone temperature.When implementing adjustments, it is recommended to use the single-factor variable method, adjusting only one parameter at a time and fully evaluating the effect, to avoid simultaneous changes of multiple parameters making the cause of the problem untraceable.The adjustment amplitude should be small rather than large; each adjustment is recommended to be controlled within 5%~10% of the original value, and after adjustment run stably for at least 3~5 mold cycles to observe the effect. 2. Check raw material purity.Inspection work should establish a standardized checklist, specifying inspection items, technical standards, inspection frequency and responsible persons.Key equipment components should be regularly disassembled to check the condition of hidden parts, and judgment should not be based solely on operating appearance.Inspection results should be recorded in detail and a trend analysis mechanism established to predict potential failures. It is recommended to formulate a preventive checklist for the Gel particles on the parison surface (fisheyes) problem, incorporate parison wall thickness uniformity and transfer temperature control into the daily inspection scope, and conduct online monitoring of key parameters through the SPC statistical process control method to achieve early warning and rapid response to problems. In terms of material management, incoming inspection of raw materials and in-process testing of work-in-progress should be strengthened, and key performance indicators of PET, PP, HDPE and PS should be strictly controlled to ensure the stability of forming quality from the source.

In summary, the causes of the "Gel particles on the parison surface (fisheyes)" problem can be attributed to the combined action of multiple factors such as Insufficient plasticization temperature, High-melting-point resin mixed into the raw material.To solve this problem, it is necessary to start from aspects such as Raise the plasticizing zone temperature, Check raw material purity and take systematic governance measures.In actual production, it is recommended to establish a prevention and rapid response mechanism for this problem, achieving stable production and continuous improvement through parison wall thickness uniformity and transfer temperature control.