Poor Dispersion in In-situ Reinforced Blending of LCP with General-Purpose Resins
Fenómeno do problema
【Problem Phenomenon】When LCP is blend-extruded with PET/PA etc., dispersion is uneven, the reinforcement effect does not meet expectations, and unmelted particles appear in the product
Análise das causas
LCP needs to form an in-situ fibrillated reinforcing phase in a specific temperature and shear field; when the blending temperature does not match or dispersive shear is insufficient, LCP becomes island-like particles instead of microfibrils; the Buffalo review records the technical key points of LCP blending in-situ reinforcement
Solução
Set the blending temperature in the overlapping melting point range of the two resins; increase the strength of screw shear mixing elements to promote LCP fibrillation; control the LCP content in the effective fibrillation range
Conclusão principal
LCP blending reinforcement relies on the temperature window and shear fibrillation; content and process must be linked; after confirming effectiveness, solidify the parameters and practices into the work instruction to prevent recurrence