Material Drying
7 visualizações
PA6 Welding Assembly
Fenómeno do problema
Ultrasonically welded PA6 parts have insufficient weld strength, and the welding surface splashes and flashes
Análise das causas
After PA6 absorbs moisture, the moisture at the welding interface vaporizes, forming a loose weld; improper amplitude and pressure parameters cause flash splashing or insufficient fusion; glass fiber orientation also affects welding strength
Solução
①Control part moisture content before welding and weld as soon as possible; ②orthogonally optimize the three parameters of amplitude, pressure, and time; ③design energy directors on the weld line to concentrate energy; after adjustment, continuously sample to verify the effect, and resume mass production after confirming stability
Conclusão principal
Half of the success or failure of PA6 ultrasonic welding lies in moisture content; pre-weld state management plus parameter optimization plus energy director design constitutes a complete solution; after confirming effectiveness, fix the parameters and practices into the work instructions to prevent recurrence
Isto foi útil?
0 pessoas acharam isto útil
Obrigado pelo seu comentário!