PA6 Packaging Film Oxygen Barrier
Fenómeno do problema
The PA6 composite packaging film delaminates after high-temperature retorting
Análise das causas
During retorting, the PA6 layer absorbs moisture and expands, and its thermal expansion mismatches with the adhesive layer; interfacial stress under humidity and heat causes delamination; when troubleshooting on site, verify item by item according to this mechanism, and avoid blindly adjusting the machine based only on experience
Solução
Select retort-grade PA6 film and matching adhesive for retort pouches; control the lamination curing process; verify the lamination strength by a 121°C retort test; after adjustment, continuously sample to verify the effect, and resume mass production after confirming stability
Conclusão principal
Retort packaging requires matching verification of the entire retort-grade material system; after confirming effectiveness, fix the parameters and practices into the work instructions to prevent recurrence; include this case in the defect archive as a reference for troubleshooting similar problems in the future
Isto foi útil?
0 pessoas acharam isto útil
Obrigado pelo seu comentário!