PMMA Laser Cutting Edge Stress
Fenómeno do problema
Microcracks appear at sheet edges after laser cutting and propagate during subsequent use.
Análise das causas
The laser heat-affected zone generates thermal stress, and microcracks initiate at edge stress concentrations; the problem worsens when sheet internal stress is high.; During on-site troubleshooting, verify item by item according to this mechanism to avoid blindly adjusting the machine based on experience alone.
Solução
①Anneal after cutting to eliminate edge stress; ②optimize laser power and speed; ③select low-stress sheets; ④edge polishing treatment.; After adjustment, continuously sample to verify the effect, and resume mass production only after confirming stability.
Conclusão principal
The thermal influence of laser processing needs supporting post-treatment; annealing and edge treatment can eliminate crack hazards.; After confirming effectiveness, fix the parameters and practices into the work instruction to prevent recurrence.
Isto foi útil?
0 pessoas acharam isto útil
Obrigado pelo seu comentário!