Blow Molding
7 visualizações
Severe Parison Sag in PU Extrusion '2079851475616104457
Fenómeno do problema
PU extrusion '2079851475616104457 parison sag 20-40mm, causing bottle bottom wall thickness only 0.3-0.4mm
Análise das causas
PU melt strength low, parison stretched thin under gravity; parison extrusion speed slow increasing sag time; parison temperature too high, viscosity low, aggravating sag
Solução
1) Add slight crosslinking agent 0.3-0.5wt% to increase melt strength; 2) Increase parison extrusion speed to shorten sag time; 3) Reduce parison temperature by 10-15°C to increase viscosity; 4) Wall thickness controller to compensate sag
Conclusão principal
Parison sag is caused by low melt strength; slight crosslinking and wall thickness control are key