Poor Fatigue Resistance of CMC
Fenómeno do problema
Fatigue life of CMC products <10⁴ cycles, lower than the 10⁵ cycles requirement
Análise das causas
CMC elastic recovery is insufficient and plastic deformation accumulates each cycle; crosslinking degree is low and fatigue crack propagates fast
Solução
1)Increase crosslinking degree to improve recovery and reduce accumulated deformation; 2)Select high-molecular-weight grade to increase fatigue threshold; 3)Product design to reduce stress concentration
Conclusão principal
Poor fatigue resistance is caused by insufficient recovery and fast crack propagation; increasing crosslinking is the key