Material Analysis
14 visualizações
DSTDP poor weather resistance
Fenómeno do problema
After 6 months outdoors, DSTDP mechanical properties decrease 40-50%, surface cracking
Análise das causas
DSTDP polyolefin backbone photo-oxidative degradation, molecular chain scission; ultraviolet directly attacks C-C bonds
Solução
1) UV-327 0.5-1wt% to absorb ultraviolet; 2) HALS-770 0.2-0.5wt% for light stabilization; 3) 1010+168 antioxidant 0.3wt% to prevent oxidation
Conclusão principal
Poor weather resistance is caused by photo-oxidation; UV+HALS+antioxidant triple protection is key