Injection Molding
14 visualizações
Severe warpage deformation of PBT injection molded parts
Fenómeno do problema
PBT injection molded products show severe warpage after demolding, especially thin-walled large flat products.
Análise das causas
PBT has a fast crystallization rate and high crystallinity (40-60%), the shrinkage rate differs greatly in different directions (0.8-1.5% in the flow direction, 1.2-2.0% in the perpendicular direction), and the cooling of each part is uneven.
Solução
Raise the mold temperature to 80-100°C to make crystallization uniform; design the product with uniform wall thickness; optimize the gate position to balance the flow; use glass fiber reinforcement to reduce anisotropic shrinkage when necessary.
Conclusão principal
PBT warpage is the result of anisotropic shrinkage caused by its high crystallinity, and needs to be addressed from mold temperature and glass fiber reinforcement.