Storage Cracking/Delayed Cracking of acrylonitrile-butadiene-styrene copolymer PS Products
Fenómeno do problema
PS products crack several hours or days after processing, i.e., delayed cracking, caused by the slow release of residual stress.
Análise das causas
（1）The residual stress of the product is large, and the stress is released over time, leading to cracking
（2）The product wall thickness is uneven, and the internal stress at the thick-walled parts is large
（3）The mold temperature is too low, the cooling speed is fast, and the residual stress is high
（4）Improper demolding produces mechanical damage that becomes a crack source
（5）Environmental temperature changes accelerate stress release
Solução
（1）Increase the mold temperature to reduce residual stress
（2）Optimize the product design with uniform wall thickness
（3）Annealing treatment (60-80°C, 1-4h) releases the stress
（4）Ensure uniform force during demolding
（5）Store the products in a constant-temperature environment
Conclusão principal
PS delayed cracking is caused by the slow release of residual stress.