Molds & Tooling
12 visualizações
Product stress cracking
Fenómeno do problema
Fine cracks appear on the surface of PEI products during placement or use
Análise das causas
Large internal stress generated during molding; mold temperature too low <120°C, quenching freezes the stress; the product geometry has stress concentration features such as sharp corners
Solução
Increase the mold temperature to 150-180°C to slow cooling; anneal the product after demolding at 200°C/2h to eliminate internal stress; optimize product design to avoid sharp corners and abrupt cross-section changes
Conclusão principal
Annealing is an effective method to eliminate internal stress and prevent cracking in PEI products