Problema e solução

Q

Product Cracking/Cracks

A

The essence of cracking is that the internal stress exceeds the material strength limit, and it needs to be addressed from two aspects: reducing stress concentration and improving material toughness.

Extrusion & Post cooling rate demolding internal stress cracking

Q

Surface Orange Peel/Roughness

A

Surface defects are the result of the combined effects of mold condition, process parameters, and material formula, and each factor needs to be systematically investigated and optimized in a targeted manner.

Molds & Tooling demolding surface orange peel roughness

Q

Surface Flow Marks/Ripples

A

Surface defects are the result of the combined effects of mold condition, process parameters, and material formula, and each factor needs to be systematically investigated and optimized in a targeted manner.

Molds & Tooling casting mold temperature gel

Q

Product Warpage and Deformation

A

The deformation problem stems from internal stress caused by uneven shrinkage or heating in various parts of the product, and needs to be systematically solved from three aspects: structural design, process parameters, and post-treatment.

Molds & Tooling cooling rate mold temperature deformation internal stress demolding

Q

Product Shrinkage/Shrinkage Cavities

A

The core of shrinkage defects lies in the contradiction between material curing volume change and insufficient process compensation, which needs to be comprehensively controlled through formula optimization and process adjustment.

Molds & Tooling casting shrinkage rate demolding

Q

Runaway Exotherm/Explosive Polymerization

A

This problem requires comprehensive analysis from multiple dimensions of materials, processes, equipment, and operation, and should be solved by systematically optimizing process parameters and the quality control system.

Processing Machinery casting exotherm catalyst cracking

Q

Incomplete Curing of the Product/Long-Term Tackiness

A

The core of the poor curing problem is that the chemical reaction conditions are not met, and the formula ratio and curing process parameters need to be precisely controlled.

Molds & Tooling curing time curing agent mold temperature demolding

Q

Insufficient Casting/Incomplete Filling

A

This problem requires comprehensive analysis from multiple dimensions of materials, processes, equipment, and operation, and should be solved by systematically optimizing process parameters and the quality control system.

Molds & Tooling casting viscosity gel

Q

Surface Bubbles/Voids on the Product

A

The essence of this problem is that gas is not effectively removed during the casting '2079851475616104453, and it needs to be solved collaboratively from three aspects: degassing process, casting method, and venting design.

Material Drying degassing bubbles casting

Q

Product Chalking After Outdoor Use

A

In summary, the causes of the 「Product Chalking After Outdoor Use」 problem can be attributed to the combined effects of multiple factors such as poor weather resistance of the resin and no UV stabilizer added. To solve this problem, it is necessary to start from aspects such as adding UV stabiliz...

Material Drying Product Chalking After Outdoor Use rotational molding resin properties thermal stability