Stretch rod scratching the bottle inner wall

In the stretch '2079851475616104457 production process, the product exhibits the quality defect of "Stretch rod scratching the bottle inner wall". The specific manifestation is that scratches caused by the stretch rod appear on the inner wall of the bottle body. This defect is relatively common when processing materials such as PET, PP, PC, and its occurrence conditions are usually related to the unreasonable settings of stretching temperature, stretch ratio, blowing pressure, and preform heating uniformity. When the "Stretch rod scratching the bottle inner wall" situation is severe, it will cause a series of chain quality defects in the product in terms of appearance, dimensional accuracy, mechanical properties, etc., which not only reduces the functionality and safety of the product in use, but also directly increases the scrap rate and production cost. Therefore, this problem requires systematic diagnosis and optimization from multiple dimensions such as material selection, the status of the stretch '2079851475616104457 machine, heating oven, stretch rod, and blow mold, and stretching temperature, stretch ratio, blowing pressure, and preform heating uniformity.

1. Stretch rod surface rough or damaged. This factor causing the problem reflects that certain process conditions or material characteristics in stretch blow '2079851475616104453ing have not met the optimal molding requirements. Such problems are often cumulative and hidden, and should be investigated and verified as key focus items during process debugging and finalization to ensure that hidden dangers are eliminated at the source. 2. Insufficient stretch rod lubrication. This factor causing the problem reflects that certain process conditions or material characteristics in stretch blow '2079851475616104453ing have not met the optimal molding requirements. Such problems are often cumulative and hidden, and should be investigated and verified as key focus items during process debugging and finalization to ensure that hidden dangers are eliminated at the source. In addition, the insufficient overall coordination of preform heating uniformity and biaxial stretch orientation control is also a factor that cannot be ignored; there are complex interactions and coupling relationships among the process parameters, and the deviation of any one parameter may aggravate the degree of "Stretch rod scratching the bottle inner wall" through chain effects. In terms of equipment maintenance, the regular overhaul and precision confirmation of the stretch '2079851475616104457 machine, heating oven, stretch rod, and blow mold are not in place, causing the actual operating parameters of the equipment to deviate from the process requirements, which will also become a potential inducement of the "Stretch rod scratching the bottle inner wall" problem.

1. Polish the stretch rod surface. Polishing operations should be carried out step by step from coarse to fine; each time a finer abrasive is changed, the polishing direction should be changed to eliminate the texture traces of the previous step. The final surface roughness should be tested with a roughness meter to confirm it meets the standard. After polishing is completed, it should be thoroughly cleaned to remove abrasive and grinding agent residues to prevent them from entering the melt and contaminating the product. 2. Repair the damaged areas. Polishing operations should be carried out step by step from coarse to fine; each time a finer abrasive is changed, the polishing direction should be changed to eliminate the texture traces of the previous step. The final surface roughness should be tested with a roughness meter to confirm it meets the standard. After polishing is completed, it should be thoroughly cleaned to remove abrasive and grinding agent residues to prevent them from entering the melt and contaminating the product. 3. Ensure the stretch rod is clean and smooth. Cleaning work should be incorporated into the equipment preventive maintenance plan, and the cleaning frequency should be reasonably determined according to the actual conditions of the processing materials and operating cycle. Use dedicated cleaning tools and cleaning materials to avoid scratching the cavity surface or electrolytic corrosion caused by improper operation. After cleaning, recheck and confirm that the key clearances are accurate. In terms of material management, incoming inspection of raw materials upon arrival and in-process inspection of work-in-progress should be strengthened, and the key performance indicators of PET, PP, PC should be strictly controlled to ensure the stability of molding quality from the source.

In summary, the causes of the "Stretch rod scratching the bottle inner wall" problem can be attributed to the combined action of multiple factors such as Stretch rod surface rough or damaged, Insufficient stretch rod lubrication. Solving this problem requires starting from aspects such as Polish the stretch rod surface, Repair the damaged areas and adopting systematic governance measures. In actual production, it is recommended to establish a prevention and rapid response mechanism for this problem, and achieve stable production and continuous improvement through preform heating uniformity and biaxial stretch orientation control.