Electrostatic discharge marks on the product surface

In the extrusion '2079851475616104457 production process, the product exhibits the quality defect of "Electrostatic discharge marks on the product surface".The specific manifestation is Dendritic discharge marks appear on the product surface.This defect is more common when processing materials such as HDPE, PP, PVC and PC, and its occurrence is usually related to unreasonable settings of melt temperature, extrusion speed, blowing pressure and mold temperature.When the Electrostatic discharge marks on the product surface situation is severe, it will cause a series of chain quality defects in the product's appearance, dimensional accuracy, mechanical properties and other aspects, which not only reduces the product's functionality and safety in use, but also directly increases the scrap rate and production cost.Therefore, this problem requires systematic diagnosis and optimization from multiple dimensions such as material selection, the status of the extruder, head, die, mold clamping mechanism and blowing system, and melt temperature, extrusion speed, blowing pressure and mold temperature.

1. Discharge breakdown of the surface after high static accumulation.This factor causing the problem reflects that certain process conditions or material properties in extrusion '2079851475616104457 do not meet the optimal forming requirements.Such problems are often cumulative and concealed, and should be investigated and verified as key focus items during process debugging and finalization to ensure hidden dangers are eliminated at the source. In addition, the insufficient overall coordination of parison wall thickness control and parison temperature uniformity is also a factor that cannot be ignored; there are complex interactions and coupling relationships among the process parameters, and the deviation of any parameter may aggravate the degree of Electrostatic discharge marks on the product surface through chain effects.

1. Install a static eliminator.Installation of equipment or accessories should strictly follow the installation manual; key mating surfaces must be cleaned and checked for damage before installation.Fastening bolts should be tightened evenly according to the specified torque values and diagonal sequence; after installation, use precision measuring tools to verify whether the installation accuracy meets technical requirements. 2. Increase ambient humidity.When implementing adjustments, it is recommended to use the single-factor variable method, adjusting only one parameter at a time and fully evaluating the effect, to avoid simultaneous changes of multiple parameters making the cause of the problem untraceable.The adjustment amplitude should be small rather than large; each adjustment is recommended to be controlled within 5%~10% of the original value, and after adjustment run stably for at least 3~5 mold cycles to observe the effect. 3. Use antistatic masterbatch.Before introducing new tools, new materials or new methods, sufficient applicability evaluation and small-batch verification should be carried out.It is recommended to first conduct offline tests or simulation analyses outside production conditions, and introduce them into the formal production line only after confirming effectiveness and safety.Keep proper change management records to facilitate subsequent traceability and experience accumulation. In terms of material management, incoming inspection of raw materials and in-process testing of work-in-progress should be strengthened, and key performance indicators of HDPE, PP, PVC and PC should be strictly controlled to ensure the stability of forming quality from the source.

In summary, the causes of the "Electrostatic discharge marks on the product surface" problem can be attributed to the combined action of multiple factors such as Discharge breakdown of the surface after high static accumulation.To solve this problem, it is necessary to start from aspects such as Install a static eliminator, Increase ambient humidity and take systematic governance measures.In actual production, it is recommended to establish a prevention and rapid response mechanism for this problem, achieving stable production and continuous improvement through parison wall thickness control and parison temperature uniformity.