Injection Molding
6 görüntüleme
Warpage in PU '2079851475616104452
Sorun Belirtisi
PU injection molded products warp 2-3mm/100mm after demolding, flatness not up to standard
Neden Analizi
PU shrinkage large and mold temperature uneven causing shrinkage differences in each direction; gate location improper, flow orientation stress unevenly released; cooling time insufficient
Çözüm
1) Increase mold temperature to 40-60°C to reduce temperature difference; 2) Increase holding pressure 50-70MPa; 3) Optimize gate location for uniform flow; 4) Extend cooling time; 5) Annealing to release residual stress
Temel Çıkarım
Warpage is caused by shrinkage differences and orientation stress; uniform mold temperature and holding are key