Molding Process
8 görüntüleme
Glass Fibre large compression set
Sorun Belirtisi
Glass Fibre product compression set >30%, below the 15% requirement
Neden Analizi
Glass Fibre elastic recovery insufficient; crosslinking degree too low, plastic deformation unrecoverable; density too low, cell walls thin, recovery poor
Çözüm
1) Raise crosslinking degree to 60-70% to reduce plastic deformation; 2) select high elastic recovery Glass Fibre grade; 3) add reinforcing filler
Temel Çıkarım
Large compression set is caused by insufficient crosslinking; raising crosslinking degree is key