Molding Process
3 visualizações
Glass Fibre large compression set
Fenómeno do problema
Glass Fibre product compression set >30%, below the 15% requirement
Análise das causas
Glass Fibre elastic recovery insufficient; crosslinking degree too low, plastic deformation unrecoverable; density too low, cell walls thin, recovery poor
Solução
1) Raise crosslinking degree to 60-70% to reduce plastic deformation; 2) select high elastic recovery Glass Fibre grade; 3) add reinforcing filler
Conclusão principal
Large compression set is caused by insufficient crosslinking; raising crosslinking degree is key