Solution for insufficient lubrication of calcium-zinc stabilizer in foaming regulation
A
The insufficient lubrication problem of the calcium-zinc system in the foaming regulation stage requires comprehensive solution of formulation and process.
Production & Quality calcium-zinc stabilizerfoaming regulationinsufficient lubricationlubrication
2 görüntüleme
Tam Yanıtı Oku →
Q
Solution for hauling speed of calcium-zinc stabilizer in transparency improvement
Q
MP Internal Inclusions
A
Inclusions are caused by raw material and environmental contamination; filtration and environmental control are key
Production & Quality MPInclusionsRaw Material FiltrationEnvironmental CleaningRecycled Material Sorting
2 görüntüleme
Tam Yanıtı Oku →
Q
MP surface blooming exudation
A
blooming is caused by low molecular migration exudation; selecting a high molecular weight grade is fundamental
Production & Quality MP blooming low molecular migration high molecular weight lubricant exudation
2 görüntüleme
Tam Yanıtı Oku →
Q
MP stress cracking
A
stress cracking is caused by stress-accelerated chemical attack; annealing and high MW are key
Production & Quality MP stress cracking environmental stress annealing high molecular weight
2 görüntüleme
Tam Yanıtı Oku →
Q
MP surface microcracks
A
microcracks are caused by excessive internal stress; annealing and crack-resistant design are key
Production & Quality MP microcrack internal stress annealing stress concentration design
2 görüntüleme
Tam Yanıtı Oku →
Q
MP performance degradation after repeated processing
A
performance degradation from multiple processing is caused by thermo-mechanical degradation; limiting regrind and replenishing antioxidants are key
Production & Quality MP recycling performance degradation antioxidant replenishment thermal degradation shear degradation
2 görüntüleme
Tam Yanıtı Oku →
Q
MP products yellowing after processing
A
yellowing is caused by thermal/photo-oxidation and metal catalysis; improving the antioxidant system and UV absorber is key
Production & Quality MP yellowing thermal oxidation antioxidant UV absorber metal catalysis
2 görüntüleme
Tam Yanıtı Oku →
Q
Glass Fibre internal inclusions
A
Inclusions are caused by raw material and environmental contamination; filtration and environment control are key
Production & Quality Glass Fibreinclusionsraw material filtrationenvironment cleanlinessrecycled sorting
2 görüntüleme
Tam Yanıtı Oku →