ظاهرة المشكلة
Glass Fibre product fatigue life <10⁴ cycles, below the 10⁵ cycles requirement
تحليل الأسباب
Glass Fibre elastic recovery insufficient, each cycle accumulates plastic deformation; crosslinking degree too low, fatigue crack propagates fast
الحل
1) Raise crosslinking degree to improve recovery and reduce accumulated deformation; 2) select high molecular weight grade to raise fatigue threshold; 3) product design reduces stress concentration
الخلاصة الأساسية
Poor fatigue resistance is caused by insufficient recovery and fast crack propagation; raising crosslinking is key