PA66 dynamic mold temperature application
Fenómeno del problema
PA66 high-gloss appearance parts with conventional mold temperature always have weld lines and flow marks
Análisis de la causa
Under constant mold temperature the melt front cools forming a condensation layer, flow marks and weld lines hard to eliminate; during on-site troubleshooting, verify item by item according to this mechanism, and avoid blindly adjusting the machine based solely on experience
Solución
High-gloss parts use rapid-heat rapid-cool dynamic mold temperature: mold surface rapidly heated above 130℃ before filling, rapidly cooled to set after filling; after adjustment, continuously sample to verify the effect, and resume mass production only after confirming stability
Conclusión clave
Dynamic mold temperature trades cycle and energy costs for high surface quality; after confirming effectiveness, fix the parameters and practices into the work instruction to prevent recurrence; include this case in the defect archive as a troubleshooting reference for subsequent similar problems