Extrusion & Post
2 visualizaciones
PCABS Delamination and Peeling
Fenómeno del problema
[Problem Phenomenon] PC/ABS products peel between layers and crack along layers when bent
Análisis de la causa
Excessively low melt temperature causes two-phase separation, excessive shear causes delamination, and material contamination; the two-phase structure of PC/ABS is sensitive to the process; during on-site troubleshooting, verify item by item according to this mechanism, and avoid blindly adjusting the machine based only on experience
Solución
Increase melt temperature to ensure uniform melting; reduce excessive shear; check material contamination; after adjustment, continuously sample to verify the effect, and resume mass production after confirming stability; change only one variable at a time and record parameter changes to facilitate locating effective measures
Conclusión clave
For PC/ABS delamination, check melt temperature and shear; contamination also causes layer separation; after confirming effectiveness, fix the parameters and practices into the work instruction to prevent recurrence; include this case in the defect archive as a troubleshooting reference for similar problems in the future
¿Le ha resultado útil?
0 personas encontraron esto útil
¡Gracias por sus comentarios!