Low EAA elongation at break
Fenómeno del problema
EAA product elongation at break <100% below the 200% requirement
Análisis de la causa
EAA molecular weight too low, short chains with insufficient entanglement; excessive orientation causing extremely low transverse elongation; excessive crosslinking restricting chain slippage
Solución
1) Select high molecular weight EAA to increase entanglement density; 2) Reduce orientation by lowering injection speed; 3) Control crosslinking degree to avoid excess
Conclusión clave
Low elongation at break is caused by low molecular weight and orientation; selecting high MW and reducing orientation is key