Molding Process
4 visualizaciones
EEA Large Compression Set
Fenómeno del problema
EEA product compression set >30%, lower than the 15% requirement
Análisis de la causa
EEA elastic recovery insufficient; crosslinking degree low, plastic deformation unrecoverable; density low, cell walls thin, recovery poor
Solución
1) Increase crosslinking degree to 60-70% to reduce plastic deformation; 2) Select high-elastic-recovery EEA grades; 3) Add reinforcing fillers
Conclusión clave
Large compression set is caused by insufficient crosslinking; increasing crosslinking degree is key
¿Le ha resultado útil?
0 personas encontraron esto útil
¡Gracias por sus comentarios!