Production & Quality
15 visualizaciones
EMA stress cracking
Fenómeno del problema
EMA products crack within <100h under stress + chemicals
Análisis de la causa
Under stress, EMA molecular chains are attacked accelerated by chemicals; environmental stress cracking is a typical failure mode of polyolefins
Solución
1) Reduce product internal stress by annealing treatment; 2) Select high molecular weight EMA to improve ESC resistance; 3) Avoid contact with aggressive chemicals
Conclusión clave
Stress cracking is caused by stress-accelerated chemical attack; annealing and high MW are key