Large compression set of PU
Fenómeno del problema
PU product compression set >30%, below the 15% requirement
Análisis de la causa
PU elastic recovery insufficient; crosslinking degree too low, plastic deformation unrecoverable; density too low, cell walls thin, poor recovery
Solución
1) Increase crosslinking degree to 60-70% to reduce plastic deformation; 2) Select high elastic recovery PU grade; 3) Add reinforcing filler
Conclusión clave
Large compression set is caused by insufficient crosslinking; increasing crosslinking degree is key