PVA stress cracking
Fenómeno del problema
PVA product cracks under stress + chemical action in <100h
Análisis de la causa
Under stress, PVA molecular chains are attacked and accelerated by chemicals; environmental stress cracking is a typical failure mode of polyolefins
Solución
1) Reduce product internal stress by annealing treatment; 2) Select high molecular weight PVA to improve ESC resistance; 3) Avoid contact with aggressive chemicals
Conclusión clave
Stress cracking is caused by stress-accelerated chemical attack; annealing and high MW are the key