Elongation at Break of Biaxially Oriented Polypropylene Film Not Up to Standard
Fenómeno del problema
The test result of the elongation at break of the film is lower than the standard requirement, affecting the use performance of the product.
Biaxially oriented polypropylene film has strict requirements for elongation at break.
Análisis de la causa
(1) Improper selection or treatment of raw materials
(2) Improper setting of the extrusion temperature (140-170(stretching)/230-260(extrusion)°C)
(3) Unreasonable stretching process parameters (stretch ratio: longitudinal 4-6, transverse 8-10)
(4) Improper cooling conditions (chill roll 15-40°C°C)
(5) Poor dispersion of additives in the raw material
Solución
(1) Select a suitable biaxially oriented polypropylene film grade
(2) Optimize the extrusion temperature to a reasonable value within the range of 140-170(stretching)/230-260(extrusion)°C
(3) Adjust the stretch ratio to a reasonable value within the range of longitudinal 4-6 and transverse 8-10
(4) Optimize the chill roll temperature to within the range of 15-40°C°C
(5) Ensure uniform dispersion of additives
Conclusión clave
Film performance needs to be systematically optimized from three aspects: raw materials, process, and cooling.