Polyolefin plastomer film blocking/poor opening property (Variant: Enhanced Measures)
Fenómeno del problema
The film layers stick together and are difficult to separate, affecting subsequent processing and use.
Poor opening property is particularly prominent in film winding and automatic packaging, reducing production efficiency.
In particular, additional attention is needed on the original basis; this problem is more prominent and requires focused attention.
Análisis de la causa
（1）The polyolefin plastomer film has high surface tension and large interlayer adhesion
（2）The film is wound at too high a temperature and the cooling is insufficient
（3）The winding tension is too large
（4）Lack of anti-blocking agent
（5）The film is too thin and more likely to stick
（6）On the original basis, additional attention is needed: fluctuations in process parameters or changes in equipment status have aggravated this problem
Solución
（1）Add an appropriate amount of anti-blocking agent (such as silica powder 0.1-0.5%)
（2）Ensure the film is fully cooled before winding, and the winding temperature does not exceed 40°C
（3）Appropriately reduce the winding tension
（4）Add an appropriate amount of slip agent (such as oleamide 0.1-0.3%) to reduce surface friction
（5）Control the film thickness within a reasonable range
（6）And strengthen process monitoring; on the original basis, additional attention is needed to pay special attention to parameter stability
Conclusión clave
Film blocking is caused by surface tension and temperature, and needs to be solved by adding anti-blocking agents and controlling winding conditions.
Targeted preventive measures need to be taken in different production scenarios.