Glass Fibre insufficient flatness
문제 현상
Glass Fibre flat plate product flatness >0.5mm/100mm, warpage
원인 분석
Glass Fibre shrinkage rate large and different in each direction; mold cooling uneven; residual stress release causes continuous warpage
해결 방법
1) Uniform mold temperature to reduce temperature difference; 2) increase holding pressure to reduce shrinkage difference; 3) annealing to release residual stress
핵심 요약
Insufficient flatness is caused by shrinkage difference and stress; uniform cooling and annealing are key