Problembeschreibung
Glass Fibre flat plate product flatness >0.5mm/100mm, warpage
Ursachenanalyse
Glass Fibre shrinkage rate large and different in each direction; mold cooling uneven; residual stress release causes continuous warpage
Lösung
1) Uniform mold temperature to reduce temperature difference; 2) increase holding pressure to reduce shrinkage difference; 3) annealing to release residual stress
Wichtigste Erkenntnis
Insufficient flatness is caused by shrinkage difference and stress; uniform cooling and annealing are key