LCP thin-wall long-flow filling
문제 현상
LCP thin-wall (<0.3mm) micro parts are insufficiently filled.
원인 분석
Although LCP has extremely good flowability, it cools, solidifies and sets quickly during the process, especially in thin walls.
해결 방법
Further increase melt temperature to 370-390°C; mold temperature >150°C; increase injection speed.
핵심 요약
LCP thin-wall filling requires extremely high temperature.