Molding Process
4 visualizaciones
LCP thin-wall long-flow filling
Fenómeno del problema
LCP thin-wall (<0.3mm) micro parts are insufficiently filled.
Análisis de la causa
Although LCP has extremely good flowability, it cools, solidifies and sets quickly during the process, especially in thin walls.
Solución
Further increase melt temperature to 370-390°C; mold temperature >150°C; increase injection speed.
Conclusión clave
LCP thin-wall filling requires extremely high temperature.