EEA Internal Delamination Cracking
Problem Phenomenon
EEA products internally delaminate, cracking along the interface
Cause Analysis
Poor interfacial bonding between EEA and incompatible fillers or blend components; cooling shrinkage differences cause interlayer stress
Solution
1) Use compatibilizer to improve interfacial bonding; 2) Uniform cooling to reduce interlayer stress; 3) Reduce the addition of incompatible components
Key Takeaway
Internal delamination is caused by poor interface and shrinkage differences; compatibilizer and uniform cooling are key