Material Drying
2 views
Silver streaks caused by moisture during PVA processing
Problem Phenomenon
PVA injection molded product surface shows white silver streak marks
Cause Analysis
Raw material moisture content >0.05% vaporizes during high-temperature processing forming bubbles that are stretched into silver streaks; insufficient drying or moisture condensation in the hopper
Solution
1) Dry raw material at 80°C for 3-4h to moisture <0.02%; 2) Increase back pressure 0.5-1MPa for venting; 3) Reduce injection speed to avoid air entrainment; 4) Heat the hopper to prevent moisture condensation
Key Takeaway
Silver streaks are caused by moisture vaporization and stretching; drying and venting are the main countermeasures