Glass Fibre insufficient tensile strength
Problem Phenomenon
Glass Fibre product tensile strength 15-20% below standard value
Cause Analysis
Glass Fibre molecular weight too low, strength foundation insufficient; filler interface poor, no reinforcing effect; excessive orientation, longitudinal strong, transverse weak
Solution
1) Select high molecular weight Glass Fibre grade; 2) filler coupling agent treatment to improve interface; 3) reduce orientation to reduce longitudinal-transverse difference
Key Takeaway
Insufficient tensile strength is caused by molecular weight and poor interface; selecting high MW grade is key