5000W ABS
High Gloss, High Liquidity, Home Appliance Parts
TTC
Taiwan - China
1 Ton MOQ
7-14 Days
Product Features
Product Type
Raw Material
Category
ABS
CAS No.
9003-56-9
Manufacturer
TTC
Grade
5000W
Origin
Taiwan - China
Color
White
Packing
25.00/KG Standard Packaging
Usage level
Electronic Appliance
Feature level
High Gloss
Import
NO
Shape
Particle
Processing Method
Injection Molding
TDS — Technical Data Sheet
Rheological properties
| Property | Value | Standard | Method |
|---|---|---|---|
| Specific Gravity | 1.04 g/cm³ | 23℃ | ASTM D792 |
| Melt Volume Rate | 1.8 g/10min | 200℃,5kg | ASTM D1238 |
| Melt Volume Rate | 20 g/10min | 200℃,10kg | ASTM D1238 |
Mechanical Properties
| Property | Value | Standard | Method |
|---|---|---|---|
| Izod Impact Strength | 19 Kg-cm/cm | 23℃ 1/4" Notched | ASTM D256 |
| Izod Impact Strength | 21 Kg-cm/cm | 23℃ 1/8" Notched | ASTM D256 |
| Tensile Strength at Yield | 450 kg/cm² | 23℃,5mm/min | ASTM D638 |
| Tensile Strength at Break | 380 kg/cm² | 23℃,5mm/min | ASTM D638 |
| Elongation at Break | 30 % | 23℃,5mm/min | ASTM D638 |
| Flexural Yield | 790 kg/cm² | 23℃,2.8mm/min | ASTM D790 |
| Flexural Modulus | 27000 kg/cm² | 23℃,2.8mm/min | ASTM D790 |
Thermal properties
| Property | Value | Standard | Method |
|---|---|---|---|
| Heat Distortion Temperature | 85 ℃ | unannealing 1.8MPa | ASTM D648 |
| Vicat Softening Temperature | 103 ℃ | 1 Kg,50 ℃/hr | ASTM D1525 |
Physical Property
| Property | Value | Standard | Method |
|---|---|---|---|
| Rockwell Hardness | 115 R-scale | 23℃ | ASTM D785 |
| Mold Shrinkage | ≦ 0.4 % | 60×60×2mm SFlow | ASTM D955 |
| Moisture Absorption Equilibrium | ≦ 0.3 wt % | 23℃,50%RH | ASTM D570 |
Electrical properties
| Property | Value | Standard | Method |
|---|---|---|---|
| Relative Temperature Index | 85 ℃ | 0.062 inch above | UL-746B |
| Hot Wire Ignition | 18 Secs | 0.062 inch above | UL-746A |
| High Current Arc Ignition | 200 Arcs | 0.062 inch above | UL-746A |
| Arc Tracking Rate | 0 in/min | 0.062 inch above | UL-746A |
The supplier and grade information provided on this website is for industry indexing reference only. We are not an official agent of any third-party brand, and the displayed content does not constitute a sales offer or an agency relationship. Product authenticity, pricing, and availability are subject to the actual supplier.