EVOH Stress Cracking
Fenómeno do problema
EVOH products crack in <100h under stress + chemicals
Análise das causas
Under stress, EVOH molecular chains are attacked by chemicals at an accelerated rate; environmental stress cracking is a typical failure mode of polyolefins
Solução
1) Reduce product internal stress by annealing; 2) Select high molecular weight EVOH to improve ESC resistance; 3) Avoid contact with aggressive chemicals
Conclusão principal
Stress cracking is caused by stress-accelerated chemical attack; annealing and high MW are key