Q
MP surface microcracks
A
microcracks are caused by excessive internal stress; annealing and crack-resistant design are key
Production & Quality MP microcrack internal stress annealing stress concentration design
16 görüntüleme
Tam Yanıtı Oku →
Q
MP poor surface gloss
A
poor gloss is caused by mold roughness and crystal scattering; polishing the mold and controlling crystallization are key
Molds & Tooling MP gloss mold polishing crystal scattering nucleating agent
16 görüntüleme
Tam Yanıtı Oku →
Q
MP fast UV aging
A
fast UV aging is caused by photo-oxidation; UV absorber and HALS are key
Material Analysis MP UV aging UV absorber HALS radical scavenging
16 görüntüleme
Tam Yanıtı Oku →
Q
MP material changeover residue
A
changeover residue is caused by incomplete cleaning; thorough cleaning and disassembly are key
Processing Machinery MP changeover residue purging material screw disassembly dead zone cleaning
16 görüntüleme
Tam Yanıtı Oku →
Q
MP unstable shrinkage rate
A
unstable shrinkage rate is caused by batch differences and temperature fluctuation; raw material and temperature control are key
Material Analysis MP shrinkage rate batch difference temperature control stability crystallinity consistency
16 görüntüleme
Tam Yanıtı Oku →
Q
MP compression molding incomplete curing
A
MP thermoset curing requires the three parameters of temperature, time and pressure to be sufficient
Molding Process MP compression molding incomplete curing curing temperature curing time compression pressure
16 görüntüleme
Tam Yanıtı Oku →
Q
MP internal coarse crystallization
A
coarse crystallization is caused by slow cooling; fast cooling and nucleating agent are key
Molding Process MP coarse crystallization spherulite refinement nucleating agent cooling rate
16 görüntüleme
Tam Yanıtı Oku →
Q
MP poor weather resistance
A
poor weather resistance is caused by photo-oxidation; UV+HALS+antioxidant triple protection is key
Material Analysis MP weather resistance UV absorber HALS photo-oxidation
16 görüntüleme
Tam Yanıtı Oku →
Q
MP extruded pipe ovality exceeding standard
A
ovality is caused by uneven cooling and clamping; annular cooling and uniform haul-off are key
Extrusion & Post MP pipe ovality annular cooling vacuum sizing uniform haul-off
15 görüntüleme
Tam Yanıtı Oku →
Q
MP extruded film gel particles
A
gel particles are caused by incomplete melting; raising temperature and mixing are key
Extrusion & Post MP film gel particle melting temperature mixing section high molecular weight component
15 görüntüleme
Tam Yanıtı Oku →