Yaygın plastik malzeme zorluklarına pratik yanıtlar

Makalelere Göz At →
11636 soru
Q
EEA Processing Temperature Fluctuation
A
Temperature fluctuation is caused by improper temperature control system; PID tuning and heater band replacement are key
Material Analysis EEA temperature fluctuation PID tuning heater band thermocouple
16 görüntüleme
Tam Yanıtı Oku →
Q
EEA Insufficient Tensile Strength
A
Insufficient tensile strength is caused by molecular weight and poor interface; selecting high MW grades is key
Material Analysis EEA tensile strength molecular weight coupling agent orientation control
16 görüntüleme
Tam Yanıtı Oku →
Q
EEA Screw Slipping
A
Screw slipping is caused by premature melting; cooling the feeding section is key
Extrusion & Post EEA screw slipping feeding section temperature premature melting flight deepening
15 görüntüleme
Tam Yanıtı Oku →
Q
EEA Large Dimensional Change with Temperature
A
Dimensional temperature sensitivity is caused by the large thermal expansion coefficient; adding filler and annealing are key
Extrusion & Post EEA dimensional temperature sensitivity thermal expansion coefficient rigid filler annealing treatment
15 görüntüleme
Tam Yanıtı Oku →
Q
EEA Hardness Too High
A
High hardness is caused by crystallization and filler; adjusting cooling and filler are key
Material Analysis EEA high hardness crystallinity filler amount plasticizer
16 görüntüleme
Tam Yanıtı Oku →
Q
EEA Surface Tiger-Skin Stripes
A
Tiger-skin stripes are caused by unstable injection front; multi-stage injection and high mold temperature are key
Injection Molding EEA tiger-skin stripes injection speed multi-stage injection mold temperature control
15 görüntüleme
Tam Yanıtı Oku →
Q
EEA Low Elongation at Break
A
Low elongation at break is caused by low molecular weight and orientation; selecting high MW and reducing orientation are key
Material Analysis EEA elongation at break molecular weight orientation control crosslinking degree
16 görüntüleme
Tam Yanıtı Oku →
Q
EEA Large Compression Set
A
Large compression set is caused by insufficient crosslinking; increasing crosslinking degree is key
Molding Process EEA compression set crosslinking degree elastic recovery reinforcing filler
16 görüntüleme
Tam Yanıtı Oku →
Q
EEA Surface Blooming
A
Blooming is caused by low-molecular migration and exudation; selecting a high-molecular-weight grade is fundamental
Production & Quality EEA blooming low-molecular migration high molecular weight lubricant exudation
16 görüntüleme
Tam Yanıtı Oku →
Q
EEA Surface Stress Whitening
A
Stress whitening is caused by orientation and internal stress; reducing orientation and annealing are key
Molding Process EEA stress whitening orientation stress annealing treatment stress concentration
16 görüntüleme
Tam Yanıtı Oku →