Sorun ve Çözüm

Yaygın plastik malzeme zorluklarına pratik yanıtlar

Makalelere Göz At →
11636 soru
Q
EEA Fast Thermal Aging
A
Thermal aging is caused by thermal oxidation; improving the antioxidant system is key
Material Analysis EEA thermal aging thermal oxidation antioxidant high molecular weight
16 görüntüleme
Tam Yanıtı Oku →
Q
EEA Insufficient Compounding
A
Insufficient compounding is caused by improper screw design; increasing the mixing section is key
Processing Machinery EEA insufficient compounding screw mixing section kneading blocks side feeding
16 görüntüleme
Tam Yanıtı Oku →
Q
EEA Poor Fatigue Resistance
A
Poor fatigue resistance is caused by insufficient recovery and fast crack propagation; increasing crosslinking is key
Production & Quality EEA fatigue resistance crosslinking degree molecular weight stress concentration
16 görüntüleme
Tam Yanıtı Oku →
Q
EEA Obvious Surface Color Difference
A
Color difference is caused by uneven dispersion and orientation; masterbatch method and stable processing are key
Injection Molding EEA color difference color masterbatch dispersion pigment orientation temperature stability
15 görüntüleme
Tam Yanıtı Oku →
Q
EEA Incompatible with Lubricant
A
Lubricant incompatibility causes exudation; selecting a compatible lubricant is key
Material Analysis EEA lubricant exudation compatibility internal lubricant dosage control
16 görüntüleme
Tam Yanıtı Oku →
Q
EEA Length Out of Tolerance
A
Length out of tolerance is caused by unstable shrinkage rate; accurate shrinkage compensation is key
Molds & Tooling EEA length out of tolerance shrinkage rate mold compensation full cooling
16 görüntüleme
Tam Yanıtı Oku →
Q
EEA Surface Orange Peel
A
Orange peel is caused by rapid cooling and solidification; increasing mold temperature and holding pressure are key
Injection Molding EEA orange peel mold temperature holding pressure surface solidification
15 görüntüleme
Tam Yanıtı Oku →
Q
EEA Vacuum Section Material Overflow
A
Overflow is caused by low melt viscosity; lowering temperature and adding a baffle are key
Extrusion & Post EEA vacuum section overflow melt viscosity temperature reduction vent baffle
15 görüntüleme
Tam Yanıtı Oku →
Q
EEA Severe Internal Stress Concentration
A
Internal stress is caused by fast injection and uneven cooling; reducing speed, uniform cooling and annealing are key
Injection Molding EEA internal stress orientation stress annealing treatment uniform cooling
15 görüntüleme
Tam Yanıtı Oku →
Q
EEA Dense Surface Pits
A
Pits are caused by raw material impurities and mold damage; pure raw material and mold maintenance are key
Extrusion & Post EEA surface pits impurity particles mold repair pure raw material
15 görüntüleme
Tam Yanıtı Oku →
Önceki 1 ... 538 539 540 541 542 543 544 ... 1164 Sonraki