Molding Process
4 visualizaciones
Coarse internal crystallization of EAA
Fenómeno del problema
The spherulites inside EAA products are coarse >50μm, causing reduced transparency and low impact
Análisis de la causa
Cooling rate too slow <5°C/min allows spherulites to fully grow; no nucleating agent used to control crystallization
Solución
1) Increase the cooling rate to >20°C/min to refine spherulites; 2) Add 0.2-0.3wt% nucleating agent to control crystallization; 3) Lower the mold temperature to accelerate cooling
Conclusión clave
Coarse crystallization is caused by slow cooling; fast cooling and nucleating agent are the key