Production & Quality
15 visualizaciones
Poor EAA fatigue resistance
Fenómeno del problema
EAA product fatigue life <10⁴ cycles below the 10⁵ cycle requirement
Análisis de la causa
EAA elastic recovery insufficient, plastic deformation accumulating with each cycle; crosslinking degree too low, fatigue crack propagation fast
Solución
1) Increase crosslinking degree to improve recovery and reduce accumulated deformation; 2) Select high molecular weight grade to raise the fatigue threshold; 3) Product design to reduce stress concentration
Conclusión clave
Poor fatigue resistance is caused by insufficient recovery and fast crack propagation; increasing crosslinking is key