Production & Quality
15 visualizaciones
PU stress cracking
Fenómeno del problema
PU products crack under stress + chemicals in <100h
Análisis de la causa
PU molecular chains under stress are attacked accelerated by chemicals; environmental stress cracking is a typical failure mode of polyolefins
Solución
1) Reduce product internal stress by annealing; 2) Select high molecular weight PU to improve ESC resistance; 3) Avoid contact with aggressive chemicals
Conclusión clave
Stress cracking is caused by stress-accelerated chemical attack; annealing and high MW are key